| PRODUCT: Muncy White V.B.
Latex |
FORMULA NUMBER: 18Y-577 |
| OBJECT FINISHED: Sheet rock and wall board
|
WEIGHT/GALLON: 11.58 lbs.
VISCOSITY: 104-108 KU’s
GRIND: 4 Hegman
WEIGHT SOLIDS: 53.8%
V.O.C.: .52 lbs/gal.
VOLUME SOLIDS: 35.6%
COVERAGE: 571 sq ft/gal.
SUBSTRATE PREP.: Surface to be painted must sanded smooth
if needed, and clean of dirt and dust.
APPLICATION METHOD: Roll or brush
EQUIPMENT SETTINGS: Roll with a 1⁄2” nap or
larger roller. Brush with high quality brush
APPLIED OVER: Clean wall board
USED UNDER: Latex wall paint
|
RECOMMENDED REDUCTION: None
REDUCER: Water
REDUCED VISCOSITY: Use as supplied
RECOMMENDED FILM THICKNESS:
WET: 6-10 mils
DRY: 2.0-3.5 mils
FLASH TIME: 20 minutes
BAKE TIME: N/A
BAKE TEMPERATURE Air dry
OVEN TYPE: N/A
GLOSS: Flat
HARDNESS: N/A
IMPACT RESISTANCE: N/A |
REMARKS: This product was designed for use
as a one coat, interior wall paint with water vapor barrier
properties. Test on free films, as per ASTM D1653, method
A, condition B, Water Vapor Transmission, this material
averages 0.1 perms.
Do not use this product if air, paint or wall temperatures
are below 50 deg F.
This is a water based product and must be protected from
freezing during storage and transportation.
|
| DATE ISSUED: 8/30/00 |
COMPLETED BY:
S. Sander |
| Close
Window |
ARMORCHEM LLC
COMBINING TECHNOLOGY FOR THE FUTURE |
| PRODUCT: Frosted Linen
V.B. Latex |
FORMULA NUMBER:
18Z-581 |
| OBJECT FINISHED: Sheetrock and wall board
|
WEIGHT/GALLON: 11.04 lbs.
VISCOSITY: 104-108 KU’s
GRIND: 4 Hegman
WEIGHT SOLIDS: 47±2%
V.O.C.: 1.14 lb./gal.
VOLUME SOLIDS: 30±1%
COVERAGE: 480 sq.ft.@ 1.0 mil
SUBSTRATE PREP.: Surface to be painted should be sanded
smooth if needed and blown clean of dust and dirt
APPLICATION METHOD: Spray, Brush, or Roll
EQUIPMENT SETTINGS: For airless spray use 0.021”
nozzle and enough air pressure of proper atomization.
Roll with 1⁄2” nap roller. Do not over roll
or spread too thin
APPLIED OVER: Clean sheetrock
USED UNDER: Latex wall paint |
RECOMMENDED REDUCTION: None
REDUCER: Water
REDUCED VISCOSITY: Use as supplied.
RECOMMENDED FILM THICKNESS:
WET: 6.0-8.0-mils
DRY: 1.7-2.4 mils
FLASH TIME: 20 minutes
BAKE TIME: N/A
BAKE TEMPERATURE Air Dry
OVEN TYPE: N/A
GLOSS: Flat
HARDNESS: N/A
IMPACT RESISTANCE: N/A |
REMARKS:
This product was designed for one coat hide with excellent
scrub resistance and touch-up qualities. Tested in free
films, as per ASTM D-1653, Method A, Condition B, Water
Vapor Transmission, this material averages below 0.1 perms.
Do not use this product if air, paint, or surface temperatures
are below 50°F. |
DATE ISSUED: 4-29-98 |
COMPLETED BY: |
| Close
Window |
ARMORCHEM LLC
COMBINING TECHNOLOGY FOR THE FUTURE |
| PRODUCT: Frosted Linen
V.B. Latex |
FORMULA NUMBER: 18Z-581C |
| OBJECT FINISHED: Sheetrock and wall board |
WEIGHT/GALLON: 11.04 lbs.
VISCOSITY: 95-99 KU’s
GRIND: 3 Hegman
WEIGHT SOLIDS: 47±2%
V.O.C.: 1.19 lb./gal.
VOLUME SOLIDS: 30±1%
COVERAGE: 480 sq.ft.@ 1.0 mil
SUBSTRATE PREP.: Surface to be painted should be sanded
smooth if needed and blown clean of dust and dirt
APPLICATION METHOD: Spray, Brush, or Roll
EQUIPMENT SETTINGS: For airless spray use 0.021”
nozzle and enough air pressure of proper atomization.
Roll with 1⁄2” nap roller. Do not over roll
or spread too thin
APPLIED OVER: Clean sheetrock
USED UNDER: Latex wall paint |
RECOMMENDED REDUCTION: None
REDUCER: Water
REDUCED VISCOSITY: Use as supplied.
RECOMMENDED FILM THICKNESS:
WET: 8-10 mils
DRY: 2.4-3.0 mils
FLASH TIME: 20 minutes
BAKE TIME: N/A
BAKE TEMPERATURE Air Dry
OVEN TYPE: N/A
GLOSS: Flat
HARDNESS: N/A
IMPACT RESISTANCE: N/A |
REMARKS:
This product was designed for one coat hide with excellent
scrub resistance and touch-up qualities. Tested as per
ASTM E-96, this material averages below 1.0 perms.
Do not use this product if air, paint, or surface temperatures
are below 50°F. |
DATE ISSUED: 9-15-00 |
COMPLETED BY:
S. Sander |
| Close
Window |
| |
| PRODUCT: Frosted Linen
V.B. Latex |
FORMULA NUMBER: 18Z-581E |
| OBJECT FINISHED: Sheetrock and wall board |
WEIGHT/GALLON: 11.07 lbs.
VISCOSITY: 95-100 KU’s
GRIND: 3 Hegman
WEIGHT SOLIDS: 47.8%
V.O.C.: 1.15 lb./gal. (minus water)
0.41 lb/gal material VOC
VOLUME SOLIDS: 31%
COVERAGE: 495 sq.ft.@ 1.0 mil
SUBSTRATE PREP.: Surface to be painted should be sanded
smooth if needed and blown clean of dust and dirt
APPLICATION METHOD: Spray, Brush, or Roll
EQUIPMENT SETTINGS: For airless spray use 0.021”
nozzle and enough air pressure of proper atomization.
Roll with 1⁄2” nap roller. Do not over roll
or spread too thin
APPLIED OVER: Clean sheetrock
USED UNDER: Latex wall paint
|
RECOMMENDED REDUCTION: None
REDUCER: Water
REDUCED VISCOSITY: Use as supplied.
RECOMMENDED FILM THICKNESS:
WET: 8-10 mils
DRY: 2.4-3.0 mils
FLASH TIME: 20 minutes
BAKE TIME: N/A
BAKE TEMPERATURE:
Air Dry
OVEN TYPE: N/A
GLOSS: Flat
HARDNESS: N/A
IMPACT RESISTANCE: N/A |
REMARKS:
This product was designed for one coat hide with excellent
scrub resistance and touch-up qualities. Tested as per
ASTM E-96, this material averages below 1.0 perms.
Do not use this product if air, paint, or surface temperatures
are below 50°F. |
| DATE ISSUED: 5/24/2004 |
COMPLETED BY:
S. Sander |
| Close
Window |
ARMORCHEM LLC
COMBINING TECHNOLOGY FOR THE FUTURE |
| PRODUCT: ARMORCHEM 4500
GRAY DIP PRIMER |
FORMULA NUMBER:
41B-414B
|
PRODUCT DESCRIPTION:
ARMORCHEM 4500 GRAY PRIMER is an air dry, high solids,
fast drying, lead and chrome free long-oil alkyd designed
to protect steel in preconstruction exposure. The high
solids content ensures adequate protection of sharp edges,
corners and welds, while maintaining low VOC. This product
is designed for application directly to prepared steel
surfaces, and meets SSPC-Paint Specification No. 15, as
well as the performance specifications of CISC/ CPMA standard
1-73a and 2-75. |
PRODUCT CHARACTERISTICS:
Weight per Gallon: 12.02
Viscosity: 16-18 Sec
#2 Sig Zahn
Grind: 5 + Hegman
Weight Solids: 73+/-1%
Volume Solids: 50+/-1%
VOC: 3.1-3.25 lbs/gal
Gloss: 1-10 (60 Deg)
Reducer and Clean up: Mineral Spirits
Dry Time: Dust Free 30 min
Tack Free 3 hrs
Thru Dry 48 hrs
Weld Through This primer can be welded through to yield
sound welds |
PERFORMANCE CHARACTERISTICS:
The system tested (unless otherwise indicated) is steel
prepared in accordance with SSPC-SP2, dipped with one
coat of ARMORCHEM 4500 GRAY PRIMER and allowed to air
dry for 7 days.
Salt Fog Resistance: 150 hours ASTM B117
Pencil Hardness: B ASTM D3363
Direct Impact Resistance: 20 in. lb.
ASTM G14
Cyclic Salt Fog U/V Exposure: 336 hours ASTM D5894
Water Sensitivity: No Blistering ASTM D1308 |
APPLICATION PROCEDURES:
Surface must be clean, dry, and in sound condition. Remove
all dirt, loose rust, and other foreign material in accordance
with SSPC-SP2 to ensure adequate adhesion.
Application Method: Dip or Spray
Equipment Settings for Spray: Binks Model 10
#66 fluid nozzle
50-70 pressure
Minimum Recommended Film Thickness: 1.0-1.2 mil dry
Top Coat: Alkyd, 1 part Urethane, 1 part Epoxy |
REMARKS:
Refer to MSDS sheet before use. Contact your ARMORCHEM
representative for additional technical data and instructions. |
| Close
Window |
ARMORCHEM LLC
COMBINING TECHNOLOGY FOR THE FUTURE |
PRODUCT:
ARMORCHEM 4500 RED DIP PRIMER |
FORMULA NUMBER:
41B-421
|
PRODUCT DESCRIPTION:
ARMORCHEM 4500 RED PRIMER is an air dry, high solids,
fast drying, long oil alkyd designed to protect steel
in preconstruction exposure. The high solids content ensures
adequate protection of sharp edges, corners and welds,
while maintaining low VOC. This product is designed to
be applied directly to prepared steel surfaces, and meets
SSPC-Paint Specification No. 15, as well as the performance
specifications of CISC/CPMA 1-73a and 2-75. |
PRODUCT CHARACTERISTICS:
Weight per Gallon: 12.44
Viscosity: 17-18 Sec
#2 Sig Zahn
Grind: 5 + Hegman
Weight Solids: 74.5+/-1%
Volume Solids: 51.7+/-1%
VOC: 3.1-3.25 lbs/gal
Gloss: 1-10 (60 Deg)
Reducer and Clean up: Mineral Spirits
Dry Time: Dust Free 30 min
Tack Free 3 hrs
Thru Dry 48 hrs
Weld Through This primer can be welded through to yield
sound welds |
PERFORMANCE CHARACTERISTICS:
The system tested (unless otherwise indicated) is steel
prepared in accordance with SSPC-SP2, dipped with one
coat of ARMORCHEM 4500 RED PRIMER and allowed to air
dry for 7 days.
Salt Fog Resistance: 150 hours
ASTM B117
Pencil Hardness: B
ASTM D3363
Direct Impact Resistance: 20 in. lb.
ASTM G14Cyclic Salt Fog U/V Exposure: 336 hours ASTM
D5894
Water Sensitivity: No Blistering
ASTM D1308
|
APPLICATION PROCEDURES:
Surface must be clean, dry, and in sound condition. Remove
all dirt, loose rust, and other foreign material in accordance
with SSPC-SP2 to ensure adequate adhesion.
Application Method: Dip or Spray
Equipment Settings for Spray: Binks Model 10
#66 fluid nozzle
50-70 pressure
Minimum Recommended Film Thickness: 1.0-1.2 mil dry
Top Coat: Alkyd, 1 part Urethane, 1 part Epoxy |
REMARKS:
Refer to MSDS sheet before use. Contact your ARMORCHEM
representative for additional technical data and instructions. |
| Close
Window |
ARMORCHEM LLC
COMBINING TECHNOLOGY FOR THE FUTURE |
| PRODUCT: ARMORCHEM 3900
GRAY PRIMER |
FORMULA NUMBER:
41G-471A
|
PRODUCT DESCRIPTION:
ARMORCHEM 3900 GRAY PRIMER is an air dry, high solids,
fast drying, lead and chrome free medium/long-oil alkyd
designed to protect steel in preconstruction exposure.
The solids content ensures adequate protection of sharp
edges, corners and welds, while maintaining low VOC. This
product is designed for application directly to prepared
steel surfaces, and meets SSPC-Paint Specification No.
15, as well as the performance specifications of CISC/
CPMA standard 1-73a and 2-75. It is also listed under
MPI #79 Alkyd Anti-Corrosive Metal Primer. |
PRODUCT CHARACTERISTICS:
Weight per Gallon: 11.15 lbs.
Viscosity: 18-20 Sec
#2 Signature Zahn
Grind: 5 + Hegman
Weight Solids: 66.5%
Volume Solids: 43.2%
VOC: 3.73 lbs/gal
448 g/l
Gloss: 1-10 (60 Deg)
Reducer and Clean up: Mineral Spirits/Xylene
Dry Time: Dust Free 30 min
Tack Free 1 hr
Thru Dry 48 hrs
Weld Through This primer can
be welded through to yield sound welds |
PERFORMANCE CHARACTERISTICS:
The system tested (unless otherwise indicated) is steel
prepared in accordance with SSPC-SP2, dipped with one
coat of ARMORCHEM 3900 GRAY PRIMER and allowed to air
dry for 7 days.
Salt Fog Resistance: 150 hours
ASTM B117
Pencil Hardness: B
ASTM D3363
Direct Impact Resistance: 20 in. lb.
ASTM G14
Cyclic Salt Fog U/V Exposure: 336 hours
ASTM D5894
Water Sensitivity: No Blistering
ASTM D1308
|
APPLICATION PROCEDURES:
Surface must be clean, dry, and in sound condition. Remove
all dirt, loose rust, and other foreign material in accordance
with SSPC-SP2 to ensure adequate adhesion.
Application Method: Dip or Spray
Equipment Settings for Spray: Binks Model 10
#66 fluid nozzle
50-70 pressure
Minimum Recommended Film Thickness: 1.5-2.0 mil dry
Top Coat: Alkyd, 1 part Urethane, 1 part Epoxy |
REMARKS:
Refer to MSDS sheet before use. Contact your ARMORCHEM
representative for additional technical data and instructions. |
| Close
Window |
ARMORCHEM LLC
COMBINING TECHNOLOGY FOR THE FUTURE |
PRODUCT:
ArmorChem 1000SP Gray Primer |
FORMULA NUMBER:
41X-358C
|
| OBJECT FINISHED: Structural Steel |
WEIGHT/GALLON : 11.32 lbs/gal
VISCOSITY : 30" - 33" Zahn #2 Signature Cup,
78 deg. F
GRIND : 5+ Hegman
WEIGHT SOLIDS : 72.5%
V.O.C. : 3.12 lbs./gal.
VOLUME SOLIDS : 50.3%
COVERAGE : 807 sq. ft/gal @ 1.0 mil, 100% efficiency
SUBSTRATE PREP. :
Minimum SSPC-SP2, Hand Tool Clean Recommended SSPC-SP6
Commercial Blast
APPLICATION METHOD : Spray
EQUIPMENT SETTINGS : For Air spray Binks Model 18 spray
gun w/ #66 fluid nozzle and air cap. Use 50 - 70 lbs.
of air pressure.
APPLIED OVER : Clean Steel
USED UNDER : Alkyd, 1-part Urethane, or 1-part Epoxy topcoats
|
RECOMMENDED REDUCTION : NONE
REDUCER : VM & P NAPTHA
REDUCED VISCOSITY : Use as Supplied
RECOMMENDED FILM THICKNESS :
WET : 4.0 mils minimum
DRY : 2.0 mils minimum
FLASH TIME : Dust free - 5'
BAKE TIME : Tack Free - 20' Thorough dry - 10 hours
BAKE TEMPERATURE : Air Dry
OVEN TYPE: : N/A
GLOSS : 1 - 10 Degree (60 deg.)
HARDNESS : B pencil
IMPACT RESISTANCE : 20 in - lbs.
|
REMARKS:
This product was formulated as a lead and chrome free
shop primer to meet the performance requirements of the
Steel Structures Paint Council, Painting guide #7. This
product will withstand 500 hours of 5% salt fog at 2 dry
mils, and 350 hours at 1 dry mil as tested in accordance
with ASTM B 117. This coating also withstands 500 hours
of water soak and UV exposure when tested according to
ASTM D 4585. This product can be welded through to yield
sound welds. This primer can be recoated after 1 hour.
Please read Material Safety Data Sheet before Using. |
| DATE ISSUED: October 14, 2002 |
COMPLETED BY: S. Sander |
| Close
Window |
ARMORCHEM LLC
COMBINING TECHNOLOGY FOR THE FUTURE |
PRODUCT:
ArmorChem 1000SP Red Oxide Primer |
FORMULA NUMBER:
41X-359B
|
| OBJECT FINISHED: Structural Steel |
WEIGHT/GALLON : 12.15 lbs.
VISCOSITY : 30" - 33" Zahn #2
GRIND : 5 Hegman
WEIGHT SOLIDS : 75%
VOLUME SOLIDS : 52.4%
COVERAGE : 840 sq. ft/gal
SUBSTRATE PREP. :
APPLICATION METHOD : Spray
EQUIPMENT SETTINGS : For Air spray: Binks Model 18 spray
gun w/#66 fluid nozzle and air cap. Use 50 - 70 lbs. of
air pressure.
APPLIED OVER : Clean Steel
USED UNDER : Alkyd, 1-part Urethane, or 1 - part Epoxy
topcoats |
RECOMMENDED REDUCTION : NONE
REDUCER : VM & P Naphtha
Signature Cup, 78 deg. F.
REDUCED VISCOSITY : Use as Supplied
RECOMMENDED FILM THICKNESS :
V.O.C. : 3.04 lbs./gal.
WET : 4.0 mils minimum
DRY : 2.0 mils minimum
FLASH TIME : Dust free - 5'
@ 1.0 mil, 100% efficiency
BAKE TIME : Tack Free - 20'
Minimum SSPC-SP2, Hand Tool Clean Recommended SSPC-SP6,
Commercial Blast Thorough dry - 10 hours
BAKE TEMPERATURE : Air Dry
OVEN TYPE: : N/A
GLOSS : 1 - 10 Degree (60 deg.)
HARDNESS : B pencil
IMPACT RESISTANCE : 20 in - lbs.
|
REMARKS:
This product was formulated as a lead and chrome free
shop primer to meet the performance requirements of the
Steel Structures Paint Council, Painting guide #7. This
product will withstand 500 hours of 5% salt fog, at 2
dry mils and 350 hours at 1 dry mil as tested in accordance
with ASTM B 117. This product can be welded through to
yield sound welds. This primer can be recoated after 1
hour.
Please read Material Safety Data Sheet before Using. |
| DATE ISSUED: 12/30/2003 |
COMPLETED BY: S. Sander |
| Close
Window |
ARMORCHEM LLC
COMBINING TECHNOLOGY FOR THE FUTURE |
PRODUCT:
ArmorChem 1500 Universal Gray |
PRODUCT NUMBER:
41X-361 |
| OBJECT FINISHED: Structural Steel |
WEIGHT/GALLON : 12.25 lbs.
VISCOSITY : 28"-32" Zahn #2
GRIND : 5 Hegman
WEIGHT SOLIDS : 71.94 +/- 1%
VOLUME SOLIDS : 52.22 +/- .5%
COVERAGE : 838 Sq Ft/Gal
SUBSTRATE PREP. :
Minimum- SSPC-PC2 Hand tool Clean
Recommended- SSPC-PC6 Commercial Sand Blast Through dry-
12 hrs.
APPLICATION METHOD : Spray
EQUIPMENT SETTINGS : Air Spray
Binks Model 18 Spray Gun with
#66 Fluid Nozzle and Air Cap.
Use 50-60 Lbs of Air Pressure
APPLIED OVER : Steel, Aluminum
USED UNDER : Alkyd, Acrylic, 2- part Epoxy and 2-part
Urethane Topcoats |
RECOMMENDED REDUCTION: None
REDUCER : Xylene
REDUCED VISCOSITY : Use as supplied
RECOMMENDED FILM THICKNESS:
V. O. C. : 3.44 lbs/gal
WET : 4.0 Mils Minimum
DRY : 2.0 Mils Minimum
FLASH TIME : Dust Free- 10'
BAKE TIME : Tack Free- 20'
OVEN TYPE : Air Dry
GLOSS : 5-10 @ 60 Deg
HARDNESS : B Pencil
IMPACT RESISTANCE : 20 in-lbs
|
REMARKS:
This product was designed for use as a lift resistant
primer for steel
or aluminum. It is a phenolic alkyd that exhibits superior
salt spray resistance and can be used in conjunction with
2 part epoxy and urethane top coats to provide protection
to areas where rust is a severe problem. It exhibits excellent
adhesion to Ferrous and Non-Ferrous metal surfaces. This
product is lead, and Chrome Free.
Please read Material Safety Data Sheet before Using. |
| DATE ISSUED: 2/15/2007 |
COMPLETED BY: S. Sander |
| Close
Window |
ARMORCHEM LLC
COMBINING TECHNOLOGY FOR THE FUTURE |
PRODUCT:
ArmorChem 1500 Universal Red
|
PRODUCT NUMBER: 41Y-367 |
| OBJECT FINISHED: Structural Steel |
WEIGHT/GALLON : 12.43 lbs.
VISCOSITY : 28-32" Zahn #2
GRIND : 5 Hegman
WEIGHT SOLIDS : 72.3 +/- 1%
VOLUME SOLIDS : 52.2 +/- .5%
COVERAGE : 837 sq ft/gal
SUBSTRATE PREP. :
Minimum- SSP-PC2 Hand Tool Clean Through dry- 12 hrs Recommended-
SSPC-PC6 Commercial Sand Blast
APPLICATION METHOD : Spray
EQUIPMENT SETTINGS :
For air spray use a Binks Model 18
spray gun with #66 air cap and fluid
nozzle. Use 50-60 lbs of air pressure.
APPLIED OVER : Steel, Aluminum
USED UNDER : Alkyd, Acrylic Epoxy, and Urethane Topcoats |
RECOMMENDED REDUCTION: None
REDUCER : Xylene
REDUCED VISCOSITY : Use as supplied
RECOMMENDED FILM THICKNESS
V. O. C. : 3.44 lbs/gal
WET : 4 mils minimum
DRY : 2 mils minimum
FLASH TIME : Dust free- 10'
BAKE TIME : Tack free- 20'
BAKE TEMPERATURE : Air Dry
OVEN TYPE : N/A
GLOSS : 5-10 (60 deg)
HARDNESS : B pencil
IMPACT RESISTANCE : 20 in lbs. |
REMARKS:
This product was designed for use as a lift resistant
primer for steel or
aluminum. It exhibits superior salt spray resistance and
should be used in
conjunction with a high performance topcoat to provide
protection to areas
where rust is a severe problem.
Please read Material Safety Data Sheet before Using. |
| DATE ISSUED: 1/12/2004 |
COMPLETED BY:
S. Sander |
| Close
Window |
|
|
| |
|